| Alloy | Temper | UTS (Mpa) | Yield Strength (Mpa) | Elongation (%) | ||
|---|---|---|---|---|---|---|
| Minimum | Maximum | Minimum | Maximum | A 50mm (Minimum) | ||
| EN AW-1050 A | F | 60 | – | 20 | – | 23 |
| O | 60 | 95 | 20 | – | 23 | |
| Alloy | Temper | UTS(Mpa) | % Elongation | |||
| Min | Max | 0.5 mm -0.8 mm | 0.81 mm - 1.30 mm | 1.30 mm - above | ||
| 1060 | O | 55 | 75 | 25 | 25 | 30 |
| H12 | 75 | 110 | 6 | 6 | 7 | |
| H14 | 90 | 120 | 5 | 5 | 6 | |
| H16 | 95 | 130 | 4 | 4 | 4 | |
| H18 | 130 | --- | 3 | 3 | 3 | |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 7.7-8.03 | 25 | |
| Poisson's Ratio | 0.27-0.30 | 25 | |
| Elastic Modulus (GPa) | 190-210 | 25 | |
| Tensile Strength (Mpa) | 640 | 25 | cold drawn, spheroidized annealed more |
| Yield Strength (Mpa) | 495 | ||
| Elongation (%) | 10 | ||
| Reduction in Area (%) | 45 | ||
| Hardness (HB) | 192 | 25 | cold drawn, spheroidized annealed more |
| Alloy | Temper | UTS(Mpa) | % Elongation | |||
| Min | Max | 0.5 mm -0.8 mm | 0.81 mm - 1.30 mm | 1.30 mm - above | ||
| 1100 | O | 75 | 110 | 20 | 25 | 29 |
| H12 | 95 | 130 | 5 | 6 | 7 | |
| H14 | 110 | 145 | 3 | 4 | 5 | |
| H16 | 130 | 165 | 2 | 3 | 4 | |
| H18 | 150 | --- | 2 | 2 | 3 | |
| Alloy | Temper | UTS (Mpa) | Yield Strength (Mpa) | Elongation (%) | ||
| - | - | Minimum | Maximum | Minimum | Maximum | A 50mm (Minimum) |
| EN AW-2014 | O | – | 250 | – | 135 | 10 |
| T4 | 370 | – | 230 | – | 11 | |
| Material | Tensile Strength (N/mm²) min | Yield Strength | Elongation in 4D % | ||
| ksi | Mpa | ksi | Mpa | ||
| Aluminum 2017 | 55 | 379 | 32 | 221 | 12 |
| Temper | Tensile Strength | Yield Strength | Elongation |
| KSI | KSI | % | |
| (annealed) | 32 | 14 | 12 |
| T3 | 63 | 42 | 15 |
| Properties | Metric | Imperial |
| Tensile strength | 130 MPa | 18855 psi |
| Yield strength | 125 MPa | 18130 psi |
| Shear strength | 83 MPa | 12039 psi |
| Fatigue strength | 55 MPa | 7977 psi |
| Elastic modulus | 70-80 GPa | 10153-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
| Elongation | 10% | 10% |
| Hardness | 35 | 35 |
| Temper | 0.2% Proof Stress, MPa min† | Tensile Strength, MPa | Elongation % min‡ |
| O (annealed) | 35 | 105 – 145 | 12 – 22 |
| H12 | 95 | 125 – 165 | 2 – 8 |
| H14 | 115 | 145 – 185 | 1 – 6 |
| H16 | 135 | 165 – 205 | 1 – 3 |
| H18 | – | > 185 | 1 – 3 |
| H32 | 85 | 115 – 160 | 3 – 9 |
| H34 | 105 | 135 – 180 | 2 – 7 |
| H36 | 125 | 160 – 200 | 1 – 4 |
| H38 | – | > 180 | 1 – 4 |
| Hardness, Brinell | Poisson's Ratio | Melting Point | Electrical Resistivity | Modulus of Elasticity | Specific Heat |
| 47 | 0.33 | 607 - 649 °C | 4.99e-006 ohm-cm | 70.3 GPa | 0.88 J/g-°C |
| Proof Stress | Tensile Strength | Elongation at 50 mm | Hardness Brinell |
| 80 Min MPa | 190 - 260MPa | 12 Min % | 52 HB |
| Proof Stress | Tensile Strength | Hardness Brinell | Elongation |
| 125 Min MPa | 275 - 350 MPa | 75 HB | 12 Min % |
| Tensile Strengtd (PSI) | Yield Strengtd (PSI) | Shear Strengtd (PSI) | Elongation in 2″ | Brinell Hardness |
| 45,000 | 40,000 | 31,000 | 12 | 95 |
| Tensile Strength, MPa | Yield Strength 0.2%, MPa | Elongation % | Hardness HBW |
| 295 | 240 | 8 | 95 |
| Material | Temper | Tensile Strength (ksi) | Yield Strength (ksi) | Elongation in 2" % |
| Aluminium Alloy 7050 Angle (AMS 4340) | T76511 | 79 | 69 | 7 |
| Aluminium Alloy 7050 Angle (AMS 4340) | T73511 | 70 | 60 | 8 |
| Aluminium Alloy 7050 Angle (AMS 4342) | T74511 | 73 | 63 | 7 |
| Temper | Tensile | Hardness | ||||
| Ultimate | Yield | Elongation | Brinell | |||
| KSI | MPA | KSI | MPA | % | ||
| T6, T651 | 83 | 572 | 73 | 503 | 11 | 150 |
| T73, T7351 | 73 | 503 | 63 | 434 | 13 | N/A |
| Alloy | Temper | UTS (Mpa) | Yield Strength (Mpa) | Elongation (%) | ||
|---|---|---|---|---|---|---|
| - | - | Minimum | Maximum | Minimum | Maximum | A 50mm (Minimum) |
| EN AW-2014 | O | – | 250 | – | 135 | 10 |
| T4 | 370 | – | 230 | – | 11 | |
| Alloy | Temper | Tensile Strength (N/mm²) min | Yield Strength (Mpa) | Elongation in 4D % | ||
|---|---|---|---|---|---|---|
| T6 | ksi | Mpa | ksi | Mpa | A 50mm (Minimum) | |
| 2017 | T651 | 60 | – | 20 | – | 23 |
| T6511 | 60 | 95 | 20 | – | 23 | |
| Temper | Tensile Strength | Yield Strength | Elongation |
| T6 | KSI | KSI | % |
| T65 | 32 | 14 | 12 |
| T651 | 63 | 42 | 15 |
| Proof Stress | Tensile Strength | Hardness Brinell | Elongation |
| 125 Min MPa | 275 - 350 MPa | 75 HB | 12 Min % |
| Tensile Strengtd (PSI) | Yield Strengtd (PSI) | Shear Strengtd (PSI) | Elongation in 2″ | Brinell Hardness |
| 45,000 | 40,000 | 31,000 | 12 | 95 |
| Tensile Strength (psi) | Yield Strength (psi) | Elongation (% in 2") | Brinell Hardness |
| 27,000 | 21,000 | 12 | 60 |
| Material | Diameter (mm) | Tensile Strength min (N/mm²) | Yield Strength min (N/mm²) | Elongation on 5.65v % (min) |
| Alloy 6082 | < 20 | 295 | 255 | 8 |
| 20 - 150 | 310 | 270 | 8 | |
| 150 - 200 | 280 | 240 | 5 |
| Standard | Temper | Tensile | Hardness | ||||
| Aluminium 7075 | Ultimate | Yield | Elongation | Brinell | |||
| T6, T651, T6511 | KSI | MPA | KSI | MPA | % | ||
| 83 | 572 | 73 | 503 | 11 | 150 | ||
| 73 | 503 | 63 | 434 | 13 | N/A | ||
| Material | Temper | Diameter (mm) | Tensile Strength min ((N/mm²) | Yield Strength (min) (N/mm²) | Elongation on 5.65 V (min) |
| 2014 Bar | T4 | <20 | 370 | 230 | 11 |
| 2014 Bar | T4 | 20-75 | 390 | 250 | 11 |
| 2014 Bar | T4 | 75-150 | 390 | 250 | 9 |
| 2014 Bar | T4 | 150-200 | 370 | 230 | 8 |
| 2014 Bar | T6510 | 20-75 | 480 | 435 | 7 |
| 2014 Bar | T6510 | 75-150 | 465 | 420 | 7 |
| 2014 Bar | T6510 | 150-200 | 435 | 390 | 7 |
| Material | Condition | Tensile Strength (N/mm²) min | Yield Strength | Elongation in 4D % | ||
| ksi | Mpa | ksi | Mpa | |||
| 2017 | 2017-T4 Bar | 55 | 379 | 32 | 221 | 12 |
| Temper | Tensile Strength | Yield Strength | Elongation |
| KSI | KSI | % | |
| (annealed) | 32 | 14 | 12 |
| T3 | 63 | 42 | 15 |
| Properties | Proof Stress | Tensile Strength | Hardness Brinell | Elongation |
| Metric | 125 Min MPa | 275 - 350 MPa | 75 HB | 12 Min % |
| Tensile Strengtd (PSI) | Yield Strengtd (PSI) | Shear Strengtd (PSI) | Elongation in 2″ | Brinell Hardness |
| 45,000 | 40,000 | 31,000 | 12 | 95 |
| Tensile Strength (psi) | Yield Strength (psi) | Elongation (% in 2") | Brinell Hardness |
| 27,000 | 21,000 | 12 | 60 |
| Diameter or minor sectional dimension mm | Tensile Strength, MPa | Yield Strength 0.2%, MPa | Elongation % |
| 0-20 | 295 | 255 | 8 |
| 20-150 | 310 | 270 | 8 |
| 150-200 | 280 | 240 | 5 |
| Temper | Tensile | Hardness | ||||
| Ultimate | Yield | Elongation | Brinell | |||
| KSI | MPA | KSI | MPA | % | ||
| T6, T651 | 83 | 572 | 73 | 503 | 11 | 150 |
| T73, T7351 | 73 | 503 | 63 | 434 | 13 | N/A |
| Material | Temper | Diameter (mm) | Tensile Strength min ((N/mm²) | Yield Strength (min) (N/mm²) | Elongation on 5.65 V (min) |
| 2014 Pipes | T4 | <20 | 370 | 230 | 11 |
| 2014 Pipes | T4 | 20-75 | 390 | 250 | 11 |
| 2014 Pipes | T4 | 75-150 | 390 | 250 | 9 |
| 2014 Pipes | T4 | 150-200 | 370 | 230 | 8 |
| 2014 Pipes | T6510 | 20-75 | 480 | 435 | 7 |
| 2014 Pipes | T6510 | 75-150 | 465 | 420 | 7 |
| Temper | Tensile Strength | Yield Strength | Elongation |
| KSI | KSI | % | |
| (annealed) | 32 | 14 | 12 |
| T3 | 63 | 42 | 15 |
| Properties | Proof Stress | Tensile Strength | Hardness Brinell | Elongation |
| Metric | 125 Min MPa | 275 - 350 MPa | 75 HB | 12 Min % |
| Tensile Strength (PSI) | Yield Strengtd (PSI) | Shear Strengtd (PSI) | Elongation in 2″ | Brinell Hardness |
| 45,000 | 40,000 | 31,000 | 12 | 95 |
| Tensile Strength (psi) | Yield Strength (psi) | Elongation (% in 2") | Brinell Hardness |
| 27,000 | 21,000 | 12 | 60 |
| Diameter or minor sectional dimension mm | Tensile Strength, MPa | Yield Strength 0.2%, MPa | Elongation % |
| 0-20 | 295 | 255 | 8 |
| 20-150 | 310 | 270 | 8 |
| 150-200 | 280 | 240 | 5 |